Products Name | Carbide Cold Heading Punches |
---|---|
Component | Tungsten,Cobalt |
Thickness/mm | +0.3/+0.1 |
Item Name | Tungsten Carbide Wear Bars |
Usage | For Cutting |
Shape | Round |
---|---|
Usage | High Precision Cold Heading Process |
Durability | Long Service Life |
Size | Customized |
Resistance | High Temperature And Wear Resistance |
Place of Origin | Xiamen |
---|---|
Brand Name | Xincheng |
Features | High Wear Resistance/High Hardness/High Strength/Corrosion Resistance/ |
---|---|
Dimention | Customized |
Density | 14.5-15.9 G/cm3 |
Hardness | HRA 89-93 |
Fracture Toughness | 7-10 MPa·m1/2 |
Application | Cutting/ Drilling/ Milling/ Grinding |
---|---|
Diameter | 2-50mm |
Dimention | Customized |
Flexural Strength | 2800-4500MPa |
Hardness | HRA 89-93 |
Name | Cemented Carbide Rod |
---|---|
Thermal Conductivity | 80-120 W/m·K |
Hra | 92.4 |
Diameter | 2-50mm |
Standard | ISO/GB/ANSI/DIN/JIS |
Features | High Wear Resistance/High Hardness/High Strength/Corrosion Resistance/ |
---|---|
Application | Cutting/ Drilling/ Milling/ Grinding |
Dimention | Customized |
Density | 14.5-15.9 G/cm3 |
Flexural Strength | 2800-4500MPa |
Features | High Wear Resistance/High Hardness/High Strength/Corrosion Resistance/ |
---|---|
Application | Cutting/ Drilling/ Milling/ Grinding |
Density | 14.5-15.9 G/cm3 |
Hardness | HRA 89-93 |
Flexural Strength | 2800-4500MPa |
Name | Solid Carbide Gun Drill |
---|---|
HRA | 82.5-95 |
Density | 13.12-15.58 |
Cobalt Content | 5-17.5 |
Corrosion Resistance | High |
Name | Cold Heading Mold |
---|---|
Shape | Round |
Application | Cold Heading Process |
Durability | Long Service Life |
Size | Customized |